Cinnamon Oil and Chitosan Coating on Orthopaedic Implant Surface for Prevention of Staphylococcus Epidermidis Biofilm Formation
Abstract
S. Epidermidis is among the most frequently isolated microorganisms found in -infection related to implanted devices and the formation of biofilm will be more resistant compared to the planktonic form. This study was carried out to determine the effect of coating on stainless steel orthopaedic implants surfaces with cinnamon oil and chitosan as bioadhesive to prevent biofilms formation of S. Epidermidis.The rod shaped stainless steel 316 L orthopaedic implant with 5 mm diameters was coated 2 times using a mixture of cinnamon oil and chitosan 3% and 2% respectively with serial concentration of cinnamon from 0.125% to 2%. The coated implants were then put into tubes that contained bacterial suspension and incubated. Subsequently, the implants were washed with PBS solution followed by MTT soulution and isopropanol acid solution. that related to biofilm formation. The results were expressed in numbers which represents the absorbance level at ELISA readings on 575 nm (A575) wavelength.The stainless steel implant coated with chitosan and cinnamon oil 2% and 1% has lower absorbance level compared with the absorbance level of S.Epidermidis biofilm only.
This study showed that mixture of cinnamon oil and chitosan coated on the surface of stainless steel orthopaedic implant has an effect against S.Epidermidis biofilm formation with the minimum cinnamon oil concentration of 1%.
Abstract | Reference